With our ET NH Implant, you and your patients are given several benefits due to its unique nanolayer of bio-resorbable apatite coating, which has super hydrophilic properties for more successful, simple, and a predictable implant healing.
The super hydrophilic NH surface treatment helps ensuring optimal treatment outcomes with every implant you place on any type of bone.
Provides more blood contact with the increased sandblasted acid-etched (SA) surface area, so it can start to clot faster.
The same clinically effective SA surface, but enhanced with a nano-layer of bioresorbable apatite with super hydrophilic properties.
Hiossen’s ET NH (Nano-hydrophilic) provides a unique surface treatment that features a hydrophilic SA combined with a low crystalline Nano-HA. This super hydrophilic NH surface helps ensuring optimal treatment outcomes with every implant you place on any type of bone, providing faster bone healing and improved osseointegration. The super-hydrophilic surface improved wettability, significantly increasing blood adhesion. During the remodeling phase, the nanoapatite coating was absorbed and the newly formed bone was integrated into the S A surface. The results of this study demonstrate that Hiossen ETIII NH Implant greatly improves the healing process and supports functional loading after approximately four weeks.
This prospective clinical study conducted in 2018 shows the ISQ (Implant Stability Quotient) measurement for four weeks after implant placement using Hiossen ETIII NH Implant. The following table shows the mean ISQ values of implants placed on the maxilla and mandible during the clinic al study period. No implant failure or complication occurred. The high ISQ value of over 75 from implant placement indicates strong initial stability after implant placement. Throughout the osseointegration period of four weeks, the mean ISQ value improved with no stability drop.
The super-hydrophilic surface improved wettability, significantly increasing blood adhesion. During the remodeling phase, the nano apatite coating was absorbed and the newly formed bone w as integrated into the SA surface. The results of this study demonstrate that Hiossen ETIII NH Implant greatly improves the healing process and supports functional loading after approximately four weeks.
| Implant Placement | Week 1 | Week 2 | Week 3 | Week 4 | |
|---|---|---|---|---|---|
| Maxilla | 75.1 / 6.2 | 76.2 / 5.6 | 76.9 / 4.8 | 77.1 / 5.1 | 78.4 / 5.3 |
| Mandible | 79.5 7 6.4 | 80.5 / 6.3 | 80.7 / 6.4 | 81.7 / 5.2 | 82.6 / 4.8 |
| Total | 78.3 / 6.6 | 79.3 / 6.3 | 79.7 / 6.2 | 80.4 / 5.5 | 82.4 / 5.3 |
Yong-Jin Kim, Marco Tallarico. (Evaluation of the implant stability quotient for early-loaded implants with a new hydrophilic surface. EDI Journal. 2018)